Iron Vanadium80 Suppliers
Iron Vanadium Alloy Free Sample
|
Ferro Vandadium FeV composition (%)
|
|||||
|
Grade
|
V
|
Al
|
P
|
Si
|
C
|
|
FeV40-A
|
38-45
|
1.5
|
0.09
|
2.00
|
0.60
|
|
FeV40-B
|
38-45
|
2.0
|
0.15
|
3.00
|
0.80
|
|
FeV50-A
|
48-55
|
1.5
|
0.07
|
2.00
|
0.40
|
|
FeV50-B
|
45-55
|
2.0
|
0.10
|
2.50
|
0.60
|
|
FeV60-A
|
58-65
|
1.5
|
0.06
|
2.00
|
0.40
|
|
FeV60-B
|
58-65
|
2.0
|
0.10
|
2.50
|
0.60
|
|
FeV80-A
|
78-82
|
1.5
|
0.05
|
1.50
|
0.15
|
|
FeV80-B
|
78-82
|
2.0
|
0.06
|
1.50
|
0.20
|
|
Size
|
10-50mm
60-325mesh
80-270mesh & customerize size
|
||||
|
item |
value |
|
Place of Origin |
China |
|
Brand Name |
ZhenAn |
|
Model Number |
FeV50-B,FeV60-B;FeMo60;FeV50-A,FeV60-A |
|
Processing Service |
Welding, Bending, Cutting |
|
Product name |
Sponge Iron |
|
Color |
Grey |
|
Standard |
ISO9001: 2008 |
|
Purity |
60% 80% 40% |
|
Material |
100% Natural |
|
MOQ |
1 Ton |
|
Packing |
As customer's requarement |
|
Usage |
Steel Making |
|
Particle Size |
10-220mm |
FeVanadium In Industry Factory
Grade 75-80 Ferro Vanadium In Industry factory
The thermite method uses aluminum as the reducing agent and uses a low ignition method to smelt in a furnace barrel lined with an alkaline furnace. First, a small part of the mixed charge is put into the reactor, which is ignited. After the reaction begins, the remaining charges are added sequentially. It is usually used to smelt high-vanadium iron (containing 60-80% vanadium). The recovery rate is slightly lower than that of electrosilicothermal method, about 90-95%.
The role of FeV:
Ferrovanadium is an important alloy additive in the steel industry. Vanadium increases steel's strength, toughness, ductility and heat resistance. The use of vanadium in the steel industry has increased dramatically since the 1960s, accounting for 85% of vanadium consumption by 1988. The consumption of vanadium in steel accounts for 20% of carbon steel, 25% of high-strength low-alloy steel, 20% of alloy steel and 15% of tool steel.
Vanadium-containing high-strength low-alloy steel (HSLA) is widely used in the production and construction of oil and gas pipelines, buildings, bridges, tracks, pressure vessels, frames, etc. due to its high strength. At present, the application range of various vanadium-containing steels is getting wider and wider, and relevant talents are becoming more and more important.
Vanadium Ferroalloys In Industry Factory
Grade 75-80 Ferro Vanadium Factory
Alloy of Iron and Vanadium Suppliers
Hot Tags: fev50 40, China fev50 40 manufacturers, suppliers, factory, ferrovanadium 70 Dark, Iron Vanadium 40%, NITRIDED FERRO VANADIUM, Vanadium Ferroalloys 60 Dark, FeV 50, FeV 40%