introduction
The raw materials for producing graphite electrodes are petroleum coke, needle coke, and coal tar pitch.
Petroleum coke can be divided into three types according to the sulfur content: high-sulfur coke (sulfur content above 1.5%), medium-sulfur coke (sulfur content 0.5%-1.5%), and low-sulfur coke (sulfur content below 0.5%). Low-sulfur coke is generally used in the production of graphite electrodes and other artificial graphite products.
Parameters
The Graphite Electrode produced by ZhenAn is considered to be of high quality in the Chinese and international markets.
| RP (regular power) graphite electrode | ||||
| thing | unit | diameter | ||
| Φ75 - Φ3.00 | Φ350-Φ450 | Φ450-Φ500 | ||
| Resistivity≤ | micro ohms | 4.5-8.0 | 4.5-8.0 | 4.5-8.0 |
| Bending strength≥ | MPa | 8.0-18.0 | 8.0-18.0 | 8.0-18.0 |
| Elastic modulus≤ | grade point average | 8.5-12.0 | 8.5-12.0 | 8.5-12.0 |
| Bulk density ≥ | g/ cm3 | 1.60-1.80 | 1.60-1.80 | 1.60-1.80 |
| Thermal expansion coefficient (100-600 ℃ ) ≤ | x10 -6 / ℃ | 2.2-2.8 | 2.2-2.8 | 2.2-2.8 |
| Ash content ≤ | % | 0.3 | 0.3 | 0.3 |
| HP (high power) graphite electrode | ||||
| thing | unit | diameter | ||
| Φ100 - Φ400 | Φ450-Φ500 | Φ550-Φ600 | ||
| Resistivity≤ | micro ohms | 3.8-6.2 | 3.8-6.2 | 3.8-6.2 |
| Bending strength≥ | MPa | 11.0-20.0 | 11.0-20.0 | 11.0-20.0 |
| Elastic modulus≤ | grade point average | 8.0-13.0 | 8.0-13.0 | 8.0-13.0 |
| Bulk density ≥ | g/ cm3 | 1.65-1.85 | 1.65-1.85 | 1.65-1.85 |
| Thermal expansion coefficient (100-600 ℃ ) ≤ | x10 -6 / ℃ | 1.5-2.0 | 1.5-2.0 | 1.5-2.0 |
| Ash content ≤ | % | 0.3 | 0.3 | 0.3 |
| UHP (ultra high power) graphite electrode | ||||
| thing | unit | diameter | ||
| Φ300 - Φ400 | Φ450-Φ500 | Φ550-Φ700 | ||
| Resistivity≤ | micro ohms | 3.0-5.5 | 3.0-5.5 | 3.0-5.5 |
| Bending strength≥ | MPa | 12.0-25.0 | 12.0-25.0 | 12.0-25.0 |
| Elastic modulus≤ | grade point average | 16.0 | 16.0 | 16.0 |
| Bulk density ≥ | g/ cm3 | 1.70-1.90 | 1.70-1.90 | 1.70-1.90 |
| Thermal expansion coefficient (100-600 ℃ ) ≤ | x10 -6 / ℃ | 0.8-1.4 | 0.8-1.4 | 0.8-1.4 |
| Ash content ≤ | % | 0.2 | 0.2 | 0.2 |
REMARK: the above data is just on the standard of YB/T, the actual product is very different from the above. For the actual, be free to contact us, please.
Payment term: T/T OR L/C
Delivery time: Within 7 days after receiving prepayment
Service: We can supply you with free samples, a booklet, a laboratory test report, an Industry Report, etc.
Welcome to our factory and company for a visit!
application
The blanks of graphite electrodes are also used to be processed into various special-shaped graphite products such as crucibles, molds, boats, and heating elements.
contact us
ZHENAN INTERNATIOANL CO., LTD
Mobile: +86-16638297595 (WhatsApp)
Fax: +86-372-5055180
Email: hester@zaferroalloy.com
Website: www.zaferroalloy.cn
Hot Tags: premium graphite electrodes process, China premium graphite electrodes process manufacturers, suppliers, factory, manganese ferrosilicio FeMn60Si14, Industrial Silicon Powder 600mesh, Powder High Purity Silicon 98 8, Vanadium Iron 60%, Wolfram ferroalloy Powder, High Temperature Molybdenum Rod